Raise3D PLA Filaments

Raise3D PLA Filaments is a premium PLA designed for all desktop FDM/FFF printers.

It ensures consistent extrusion and prevents nozzle jams.

Physical Properties
Typical Value
Density (g/cm3 at 21.5 °C) ASTM D792 (ISO 1183, GB/T 1033)
1.2
Melt index (g/10 min) 210 °C, 2.16 kg
7.0 – 11.0
Glass transition temperature (°C) DSC, 10 °C /min
61
Crystallization temperature (°C) DSC, 10 °C/min
114
The softening temperature of filament (°C) Custom method
129 – 132
Melting temperature (°C) DSC, 10 °C/min
150

Note:
1. Tested with 3D printed specimen of 100% infill.

Mechanical Properties

Property Testing Method
Typical Value Young’s modulus (MPa) (X – Y) ASTM D638 (ISO
527, GB/T 1040) 2636 ± 330

Tensile strength (MPa) (X – Y)
ASTM D638 (ISO 527, GB/T 1040) 46.6 ± 0.9

Elongation at break (%) (X –
Y) ASTM D638 (ISO 527, GB/T 1040) 1.90 ± 0.2

Bending modulus (MPa) (X – Y) ASTM D790 (ISO 178, GB/T 9341)
3283 ± 132

Bending strength (MPa) (X – Y) ASTM D790 (ISO 178,
GB/T 9341) 85.1 ± 2.9

Charpy Impact strength (KJ/m2) (X – Y) ASTM D256 (ISO 179, GB/T 1043)
2.7 ± 0.2